>Nickel and Nickel alloy
CSI-NiCu7
CSM-NiCu7 deposits 70%Ni-30%Cu weld metal based on Monel alloy 400 with raised levelsof mananese and titanium to suppress hot cracking and porsoity. It is optimised to give thehighest as-welded ductility and strength attainable in weld metal of this type.Welding of Nickel-Copper alloy to themselves and to steel. Clad side of joints in steel cladwith Nickel-Copper alloy. Surfacing steel with Nickel-Copper alloy weld metal.
- AWS
- A5.11 ENiCu-7
- KS
- -
- JIS
- Z 3224 E Ni 4060
- EN
- ISO 14172 E Ni 4060 (NiCu30Mn3Ti)
| Applications | Welding of 70%NI-30%Cu Monel such as alloy 400. |
|---|---|
| Characteristics | CSM-NiCu7 deposits 70%Ni-30%Cu weld metal based on Monel alloy 400 with raised levels of mananese and titanium to suppress hot cracking and porsoity. It is optimised to give the highest as-welded ductility and strength attainable in weld metal of this type. Welding of Nickel-Copper alloy to themselves and to steel. Clad side of joints in steel clad with Nickel-Copper alloy. Surfacing steel with Nickel-Copper alloy weld metal. |
| Notes on usage | (1) Keep the arc as short as possible and choose the welding current as low as possible. (2) Weaving width should be within two and a half times of electrode’s diameter. (3) When the electrodes have absorbed moisture, dry them at 200~250℃ for 60minutes before use. (4) Usually, preheat is not necessary, but keep the temperature of inter-pass less then 150℃. |
| Shielding Gas | - |
| Certification | ABS | - | BV | - | |
|---|---|---|---|---|---|
| CCS | - | CWB | - | ||
| DNV | - | GL | - | ||
| JIS | - | KR | - | ||
| KS | - | LR | - | ||
| NK | - | RINA | - | ||
| TUV | - | ||||
| MSDS |  |
Handbook | |
||
| DOP Attachment | - | ||||